Electronic wire series

Serial number Product name Product grade Main uses of the product
1 90°C thermoplastic LSZH flame retardant insulation B5090  

 

 

It is suitable for instruments, meters, and signal lines
2 125°C low-smoke halogen-free flame retardant irradiated insulation B5125
3 105°C low smoke halogen-free high flame retardant irradiation insulation B5105-G
4 105°C low-smoke halogen-free flame retardant irradiation insulation B5105

 

 

Testing items

  

Unit

 B5090 B5125
Standard value Typical values Standard value Typical values
Density g/cm³ ≤1.55 1.42 ≤1.50 1.44
Shaw hardness A — 96 — 97
Tensile strength Mpa ≥9.0 11.0 ≥9.0 13.0
Elongation at break % ≥150 240 ≥160 195
Volumetric resistivity Oh · cm 1.0×1014 1.2×1015 1.0×1012 5.0×1014
Air thermal aging test ℃xh 100×168 135×168
The rate of change in tensile strength % ≤±25 +11 ≤±30 +18.0
Rate of change in elongation at break % ≤±25 -12 ≤±30 -19.0
Low temperature impact embrittlement ℃ -25 -25
Failure number individuals ≤15/30 0/30 ≤15/30 0/30
Oxygen index % ≥28 32 ≥30 34
Smoke density — —
There is flame % ≤100 55 ≤100 35
Conductivity μs/ mm| ≤10 3.5 ≤10 4.0
Dielectric strength MV/m ≥20 24 ≥20 25
PH value  

—

 ≥4.3 6.0 ≥4.3 5.6

 

 

 

Testing items

  

Unit

 B5105-G B5105
Standard value Typical values Standard value Typical values
Density g/cm³ ≤1.65 1.32 ≤1.50 1.46
Shaw hardness A — 96 — 96
Tensile strength Mpa ≥9.0 11.0 ≥7.0 13.2
Elongation at break % ≥150 190 ≥150 250
Volumetric resistivity Oh · cm 1.0×1014 4.7×1015 1.0×1014 1.8×1015
Air thermal aging test ℃xh 121×168 121×168
Tensile strength retention % ≥80 85 ≥80 90
Elongation at break % ≥80 87 ≥80 89
Low temperature impact embrittlement ℃ -25 -25
Failure number individuals ≤15/30 0/30 ≤15/30 0/30
Oxygen index % ≥35 39 ≥30 34
Smoke density — —
There is flame % ≤100 64 ≤100 58
Conductivity μs/ mm| ≤10 2.8 ≤10 3.3
Dielectric strength MV/m ≥20 26 ≥20 28
PH value  

—

 ≥4.3 6.0 ≥4.3 5.9